Hot Dip Galvanized (HDG) Square Hollow Tubes for Outdoor Corrosion Resistance
Specifications
Hot dip galvanized steel tubes are high-strength, cold formed hollow sections that are hot dip galvanized to AS/NZS 4792 and have a minimum average coating mass of 300 grams per square metre applied to both the interior and exterior of the section for superior protection.
| American Standard | Standard Name |
| A500/A500M | Standard Specification for Cold-Formed Welded and Seamless Carbon Steel Structural Tubing in Rounds and Shapes |
Hot Dip Galvanized Hollow Sections Chemical Composition
Sources American Standard A500 / A500M TABLE 1 Chemical Requirements
| Element | Composition, % | |||
| Grades A, B and D | Grace C | |||
| Heat | Product | Heat | Product | |
| Analysis | Analysis | Analysis | Analysis | |
| Carbon, max A | 0.26 | 0.3 | 0.23 | 0.27 |
| Manganese, max A | 1.35 | 1.4 | 1.35 | 1.4 |
| Phosphorus, max | 0.035 | 0.045 | 0.035 | 0.045 |
| Sulfur, max | 0.035 | 0.045 | 0.035 | 0.045 |
| Copper, min B | 0.2 | 0.18 | 0.2 | 0.18 |
| A For each reduction of 0.01 percentage point below the specified maximum for carbon, an increase of 0.06 percentage point above the specified maximum for manganese is permitted, up to a maximum of 1.50% by heat analysis and 1.60% by product analysis. B If copper-containing steel is specified in the purchase order. |
||||
Hot Dip Galvanized Hollow Sections Mechanical Properties
Sources American Standard A500 / A500M TABLE 2 Tensile Requirements
| Round structural tubing | ||||
| Grade A | Grade B | Grade C | Grade D | |
| Tensile strength, min, psi (MPa) | 45,000 (310) | 58,000 (400) | 62,000 (425) | 58,000 (400) |
| Yield strength, min, psi, (MPa) | 33,000 (230) | 42,000 (290) | 46,000 (315) | 36,000 (250) |
| Elongation in 2 in. (50 mm), min, %D | 25A | 23B | 21C | 23B |
| Shaped structural tubing | ||||
| Grade A | Grade B | Grade C | Grade D | |
| Tensile strength, min, psi (MPa) | 45,000 (310) | 58,000 (400) | 62,000 (425) | 58,000 (400) |
| Yield strength, min, psi, (MPa) | 39,000 (270) | 46,000 (315) | 50,000 (345) | 36,000 (250) |
| Elongation in 2 in. (50 mm), min, %D | 25A | 23B | 21C | 23B |
| A Applies to specified wall thicknesses (t) equal to or greater than 0.120 in. (3.05 mm). For lighter specified wall thicknesses, the minimum elongation values shall be calculated by the formula: percent elongation in 2 in. (50mm) = 56t + 17.5, rounded to the nearest percent. For A500M use the following formula: 2.2t + 17.5, rounded to the nearest percent. B Applies to specified wall thicknesses (t) equal to or greater than 0.180 in. (4.57 mm). For lighter specified wall thicknesses, the minimum elongation values shall be calculated by the formula: percent elongation in 2 in. (50 mm) = 61t + 12, rounded to the nearest percent. For A500M use the following formula: 2.4t + 12, rounded to the nearest percent. C Applies to specified wall thicknesses (t) equal to or greater than 0.120 in. (3.05 mm). For lighter specified wall thicknesses, the minimum elongation values shall be by agreement with the manufacturer. D The minimum elongation values specified apply only to tests performed prior to shipment of the tubing. |
||||
Hot Dip Galvanized Hollow Sections Manufacturing Process
Hot Dip Galvanized Hollow Sections Application
Pre-Galvanized Hollow Sections Packing & Loading
Hollow Section is transported in containers
Hollow Section is transported in containers